Up and down conversion fluorescence studies on combustion synthesized Yb3+/Yb2+: MO-Al2O3 (M=Ca, Sr and Ba) phosphors

The ytterbium ions doped MO-Al2O3 (M=Ca, Sr and Ba) phosphors have been synthesized through combustion technique and their up and down conversion fluorescence properties have been studied and compared. The samples were calcinated at different temperatures and their FTIR and XRD spectra have shown a close relationship. With 976 nm excitation all these phosphors show cooperative upconversion emission at 488 nm from the pairs of two Yb3+ ions along with an unexpected broad upconversion band in the blue green region and has been assigned to arise from the defect centers. Contrary to this upconversion emission, calcium aluminate phosphor exhibits bright and very broad down-conversion fluorescence (FWHM≈160 nm) upon UV (266 nm) excitation due to Yb2+ ions. The inter-conversion between the 3+ and 2+ valence states of Yb ion has been observed on calcinations of samples in open atmosphere and has been correlated to the emission properties. The Yb2+ ions containing calcium aluminate phosphor has been found suitable for producing broad band light in the visible region (white light). Lifetime of the emitting states of Yb3+ and Yb2+ ions have also been measured and discussed.