Low-temperature synthesis of Zn2SiO4:Mn green photoluminescence phosphor

Zn2SiO4:Mn green phosphor having comparable photoluminescence (PL) efficiency with commercial phosphor has been synthesized at 1000 °C using solid state reactions involving ZnO, silicic acid and manganese acetate. The water of crystallization attached to SiO2 in silicic acid whose dissociation at 1000 °C seem to promote the sintering efficiency of Zn2SiO4:Mn. Incremental ZnO addition and re-firing at 1000 °C promote the diffusion rate of ZnO and SiO2. The formation of a single crystalline phase of willemite structure in the samples was confirmed by powder XRD measurements. The phosphor exhibit an intense excitation band centered around 275 nm and a relatively weak excitation centered around 380 nm while the broad band green emission peaks at 524 nm. Other parameters studied include PL spectra, grain morphology, ZnO/SiO2 molar ratio, Mn concentration, co-dopant/flux and the effect of chemical forms of Mn dopant as well as silica on the PL efficiency.