White light emission from organic–inorganic hererostructure devices by using CdSe quantum dots as emitting layer

In this paper, white light emission was obtained from organic–inorganic heterostructure devices by using CdSe quantum dots as emitting layer, in which CdSe quantum dots were synthesized via a colloidal chemical approach by using CdO and Se powder as precursors. Photoluminescence of CdSe quantum dots demonstrated a white emission with a full wavelength at half maximum (FWHM) of about 200 nm under ambient conditions, and the white emission could be observed in both multilayer device ITO/PEDOT:PSS/CdSe/BCP/Alq3/Al and single-layer device: ITO/PEDOT:PSS/CdSe/Al. The broad emission was attributed to the inhomogeneous broadening. The CIE coordinates of the multilayer device were x=0.35 and y=0.40. The white-light-emitting diodes with CdSe quantum dots as the emitting layer are potentially useful in lighting applications.