Spectroscopic properties of Er3+/Yb3+ codoped fluorophosphate glasses

Er3+/Yb3+ codoped fluorophosphate glasses were prepared and their thermal stabilities, Raman spectra, absorption spectra, and fluorescence spectra were measured. It is found that proper content of NaF or PbF2 is helpful for the increase of stability against crystallization. The variation of Al(PO3)3 or NaF content in the composition affects not the maximum phonon energy but the phonon density. The introduction of PbF2 decreases the phonon energy slightly. Intense green and red upconversion luminescence was observed for the fluorophosphate glass with low phosphate content. A glass matrix for upconversion luminescence requiring neither expensive raw material nor special atmospheric conditioned preparation is provided. Infrared luminescence around 1530 nm was researched. Fluorophosphate glasses with bandwidth properties and stimulated-emission cross sections better than tellurite, germanate and silicate glasses are obtained. Through the introduction of NaF, the bandwidth properties are decreased. Through the introduction of PbF2 the gain properties are increased. On the whole, it is difficult to obtain a material with the best gain properties and bandwidth properties simultaneously. There should be a compromise between them according to the demand.