Highly efficient red phosphorescent organic light-emitting diodes based on solution processed emissive layer

Highly efficient red phosphorescent organic polymer light-emitting diodes (PhOLEDs) were fabricated based on a solution-processed small-molecule host 4,4′-bis(N-carbazolyl)-1,1′-biphenyl (CBP) by doping an iridium complex, tris(1-(2,6-dimethylphenoxy)-4-(4-chlorophenyl)phthalazine)iridium (III) (Ir(MPCPPZ)3). A hole blocking layer 1,3,5-tri(1-phenyl-1H-benzo[d]imidazol-2-yl)phenyl (TPBI) with a function of electron transport was thermally deposited onto the top of CBP layer. The diode with the structure of ITO/PEDOT:PSS (50 nm)/CBP:Ir(MPCPPZ)3 (55 nm)/TPBI (30 nm)/Ba (4 nm)/Al (120 nm) showed an external quantum efficiency (QEext) of 19.3% and luminous efficiency (LE) of 18.3 cd/A at a current density of 0.16 mA/cm2, and Commission International de IʹEclairage (CIE) coordinates of (0.607, 0.375). It was suggested that the diodes using TPBI layer exhibited nearly 100% internal quantum efficiency and one order magnitude enhanced LE or QEext efficiencies.