Dielectric characters of 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 ceramics fabricated at ultra-low temperature by the spark-plasma-sintering method

Solid solution (1 − x)Pb(Mg1/3Nb2/3)O3–xPbTiO3 shows high dielectric constant near room temperature and is an ideal capacitor material. The composition 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3, which is located near the morphotropic phase boundary, were densified by the spark-plasma-sintering method at an ultra-low temperature (700 °C). Dielectric constant measurement shows that the thus prepared sample shows higher dielectric constant at room temperature and good temperature stability in a wide temperature range. The behavior is much different from that of samples sintered by conventional method and could be ascribed to size effect.