Magnetic and thermal expansion properties of chromium-substituted lithium ferrite

The structure, magnetic, and thermal expansion properties of chromium-substituted lithium ferrite have been investigated. The lattice constant (Å) decreases linearly as a (x) = 8.32366 − 0.04338x for Li0.5Fe2.5−xCrxO4 (x = 0.0–1.0). When increasing Cr content, the initial permeability decreased gradually. The average thermal expansion coefficient of Li0.5Fe2.5−xCrxO4 (x = 0.0–1.0) varied from 15.34 to 17.77 ppm/°C, with increasing Cr content, the average thermal expansion coefficient decreased. The average thermal expansion coefficient (ppm/°C) in the range of 25–850 °C give the polynomial correlation as follows, TEC (x) = 1 7.775 − 0.216x − 0.723x2 − 1.493x3 for Li0.5Fe2.5−xCrxO4 (x = 0.0–1.0).