A new direct coagulation casting process for alumina slurries prepared using poly(acrylate) dispersant

Direct coagulation casting (DCC) of concentrated aqueous alumina slurries prepared using ammonium poly(acrylate) dispersant has been studied using MgO as coagulating agent. Addition of small amounts of MgO increased the viscosity of the concentrated alumina slurries with time and finally transformed it in to a stiff gel. Sufficient working time for degassing and casting could be achieved by cooling the slurries to a temperature of ∼5 °C after proper homogenization after the addition of MgO. The DCC slip with alumina loading in the range of 50–55 vol% showed relatively low viscosity (0.12–0.36 Pa s at shear rate of 93 s−1) and yield stress (1.96–10.56 Pa) values. The wet coagulated bodies prepared from slurries of alumina loading in the range of 50–55 vol% had enough compressive strength (45–211 kPa) for handling during mould removal and further drying. The coagulated bodies prepared from slurries of alumina loading in the range of 50–55 vol% showed linear shrinkage in the range of 4.8–2.3 during drying and 17.1–16.2 during sintering respectively. Near-net-shape alumina components with density >98% TD could be prepared by the DCC process.