Hot pressing of nanocrystalline zinc oxide compacts: Densification and grain growth during sintering

Sintering behavior of nanocrystalline zinc oxide (ZnO) powder compacts using hot pressing method was investigated. The sintering conditions (temperature and total time) and results (density and grain size) of two-step sintering (TSS), conventional sintering (CS) and hot pressing (HP) methods were compared. The HP technique versus CS was shown to be a superior method to obtain higher final density (99%), lower sintering temperature, shorter total sintering time and rather fine grain size. The maximum density achieved via HP, TSS and CS methods were 99%, 98.3% and 97%, respectively. The final grain size of samples obtained by HP was greater than that of TSS method. However, the ultra-prolonged sintering total time and the lower final density (88 ks and 98.3%) are the drawbacks of TSS in comparison with the faster HP (17 ks and 99%) method.