Effect of propellant on the combustion synthesized Sr-doped LaMnO3 powders

Lanthanum strontium manganite (LSM) powders of composition La0.7Sr0.3MnO3 are good candidates for cathode application in solid oxide fuel cells. This paper reports the synthesis of LSM powders from nitrate precursors by the combustion method, using two different propellants (urea and glycine) and varying the propellant/nitrate ratio. Thermogravimetric analysis (TGA) revealed two or three decomposition stages of the as-synthesized samples, with complete burn out of organics at about 850–900 °C. X-ray diffraction (XRD) patterns showed formation of only LSM phase for the sample synthesized with excess of urea, whereas SrCO3 and MnCO3 phases were also found for the samples prepared from glycine. The powder is better crystallized when a homogeneous gel is formed before burning. The crystallite size calculated using the Scherrer equation is in the range of 15–20 nm. Scanning electron microscopy (SEM) revealed the presence of agglomerates, formed by fine particles of different shapes.