Phase development and dielectric responses in PMN–BNT ceramics

(1 − x)Pb(Mg1/3Nb2/3)O3–x(Bi0.5Na0.5)TiO3 ceramics were prepared by the conventional mixed-oxide method. All compositions show complete perovskite solid solutions and the structure to change from cubic to rhombohedral at x = 0.5. The dielectric constant and dielectric loss tangent were measured as a function of both temperature and frequency. The results indicated a relaxor ferroelectric behavior for all ceramics. The temperature at maximum of the dielectric constant of PMN–BNT ceramics were seen to increase with increasing BNT content. Moreover, the broadest dielectric peak occurs at x = 0.9, which leads to a morphotropic phase boundary in this system.