Synthesis of nanocrystalline ytterbium-doped yttria by citrate-gel combustion method and fabrication of ceramic materials

Nanosized ytterbium doped yttria powders were prepared by citrate-gel combustion techniques. As-synthesized precursor and calcined powders were characterized for their crystalline structure, particle size and morphologies. Nanocrystalline Yb3+:Y2O3 powders with pure cubic yttria crystal structure were obtained by calcination of as-prepared precursors at 1100 °C for 3 h. Powders obtained were well dispersed with an average particle size of 60 nm. By using the obtained powders, nearly full dense Yb3+:Y2O3 ceramics were produced by vacuum sintering at 1800 °C for 12 h. The emission spectrum of the sintered ceramics under the excitation wavelength of 905 nm illustrates that there are three fluorescence peaks locating at 976 nm, 1030 nm and 1075 nm respectively, all corresponding to the 2F5/2 → 2F7/2 transitions of ytterbium ion.