Synthesis and characterization of the SBA-15/carbon cryogel nanocomposites

The ordered mesoporous silica SBA-15 materials were synthesized using Pluronic P123 (non-ionic triblock copolymer, EO20PO70O20), under acidic conditions. SBA-15/carbon cryogel composites were obtained by sol–gel polycondensation of resorcinol and formaldehyde followed by freeze drying, and subsequent pyrolysis, in the presence of different amounts of SBA-15. For comparison purpose, SBA-15/carbon composite was also prepared using sucrose as carbon source. These materials were characterized by room temperature nitrogen adsorption–desorption measurement, X-ray diffraction, scanning electron microscopy (SEM) and Fourier transform infrared (FT-IR) spectroscopy. It was revealed that the samples have amorphous structure, high specific surface area (350–520 m2 g−1) and developed meso- as well as microporosity. The porosity of structure depends on the carbon source and Si/C ratio which can be easily controlled by varying concentration of starting solution.