Template assisted fabrication of TiO2 and WO3 nanotubes

Anodic aluminum oxide (AAO) templates with diameters of 200–500 nm were generated by anodizing a commercial aluminum (Al) substrate (99.7%) in 1 vol% phosphoric acid (H3PO4), with an applied voltage of 195 V. Titania and tungsten oxide nanotubes (NTs) were successfully grown on AAO template by the sol–gel process. Thermal gravimetric analyzer (TGA) curves showed that gel can be transfered to nanocrystalline particles after 19% weight loss of water molecule by evaporation. The results showed that the nanocrystalline TiO2 NTs presented at 200 °C, and grains grew as temperature increased. At a temperature of 550 °C, the (101), (103), (004), (112), (200), (105), and (211) planes of anatase TiO2 were detected clearly, whereas tungsten oxide NTs are amorphous after heat treatment at 200 °C or 300 °C. But the (110), (111), (002), (022), (222), and (004) planes of γ-WO3 phase can be observed obviously after the heat treatment at 400 °C.