High temperature monoclinic-to-tetragonal phase transition in magnesium doped lanthanum ortho-niobate

Magnesium doped lanthanum ortho-niobate (La0.98Mg0.02NbO4) was prepared by the molten salt synthesis method. X-ray diffraction and dilatometry methods were used to study high temperature behavior of the ceramic material. Special attention was paid to the phase transition between the monoclinic and tetragonal phases. The values of spontaneous strain on the basis of unit cell parameter, obtained by Rietveld refinement, have been calculated as well as Landau order parameter. The thermal expansion coefficient (TEC) of La0.98Mg0.02NbO4 was determined to be 12×10−6 1/K and 8×10−6 1/K below and above 500 °C, respectively.