Solution calorimetric investigation of AgCl–AgI ionic conductor composites at 298 K: observation of metastable AgI modifications Original Research Article

The enthalpies of solution of pure silver halides AgCl and AgI and a composite material with molar composition 0.5 AgCl–0.5 AgI were measured at 298 K in a mixture of Na2S2O3 (1 M) and NH4OH (1 M). X-ray diffraction patterns showed that the composite material contained the metastable γ-AgI phase; different mechanisms for its stabilization were discussed. The phase transition enthalpies of AgI modifications and the enthalpy of formation of the composite material were deduced from the measurements. The latter could be related to a change of interfacial enthalpies.