Characterization of structural modifications in poly-tetra-fluoroethylene induced by electron beam irradiation Original Research Article

The effects of electron beam irradiation doses on the poly-tetra-fluoroethylene (PTFE) have been studied. Several techniques, such as X-ray diffraction (XRD), differential scanning calorimetry (DSC), mechanical properties and Fourier transform infrared spectroscopy (FTIR) were applied to characterize the PTFE samples and to study the radiation effects on the crystal structure of the polymer. The irradiation dose up to 150 kGy showed an increase in the crystallinity degree of PTFE, which has been observed and confirmed during the DSC and XRD measurements. The increase in crystallinity was attributed to the scissions of the chain in the amorphous region. Moreover, the number-average molecular weights were estimated from the heat of crystallization measured by DSC technique. The results indicated that the molecular weights were decreased by increasing the heat of crystallization due to irradiation with doses up to 150 kGy. Radiation resistance of the irradiated and non-irradiated PTFE was investigated during its mechanical properties at room temperature. The dose at half value of the elongation at break is about 3.10 kGy while the dose at half value of the tensile strength is about 1.70 kGy.