Characterization of Cu(In,Ga)Se2 thin films prepared by evaporationfrom ternary compounds Original Research Article

Thin films of Cu(In,Ga)Se2 were fabricated by evaporation from ternary CuGaSe2 and CuInSe2 compounds for photovoltaic device applications and their properties were investigated. From XRF analysis, the Cu:(In+Ga):Se atomic ratio in all thin films was approximately 1:1:2. The Ga/(In+Ga) atomic ratio in the thin films changed linearly from 0 to 1.0 with increasing the [CGS]/([CGS]+[CIS]) mole ratio in the evaporating materials. However, for thin films prepared at the [CGS]/([CGS]+[CIS]) mole ratio above 0.4, the composition by EPMA analysis was not consistent with that by XRF analysis. The result of EPMA analysis showed that the surface of a thin film was Cu-rich. XRD studies demonstrated that the thin films prepared at the [CGS]/([CGS]+[CIS]) mole ratio under 0.2 had a chalcopyrite Cu(In,Ga)Se2 structure and the preferred orientation to the 112 plane. On the other hand, XRD patterns of the thin films produced at the [CGS]/([CGS]+[CIS]) mole ratio above 0.6 showed the diffraction lines from a chalcopyrite Cu(In,Ga)Se2 and a foreign phase. The separation of a peak was observed near 2θ=27°, indicative the graded Ga concentration in Cu(In,Ga)Se2 thin film.