Magnetic and dielectric properties of Ni0.8Co0.1Cu0.1Fe2O4+PZT composites Original Research Article

Magnetoelectric composites of Ni0.8Co0.1Cu0.1Fe2O4 and Lead Zirconate Titanate (PZT) were prepared by using conventional ceramic method. The measured values of saturation magnetization (M s) and magnetic moments (μ B) are in accordance with the volume fraction of ferrite content in the composite. The dielectric constant of the composites decreases with frequency. The plots of dielectric constant (View the MathML sourceεr′) against temperature (T) show a peak at their respective transition temperatures. The ME output was measured by varying dc bias magnetic field. A large ME output signal of 776 mV/cm was observed for 35% ferrite +65% ferroelectric composite. The magnetoelectric (ME) response is found to be dependent on the content of ferrite phase.