Synthesis, characterization and microwave absorption properties of titania-coated barium ferrite composites Original Research Article

Anatase titania-coated barium ferrite composites were prepared by a heterogeneous precipitation method in the presence of barium ferrite particles. The obtained samples were characterized by ξ-pH, TEM, EDX and XRD. The complex permittivity and permeability were studied in the frequency range of 2–12 GHz. The structure and microwave response properties are investigated. The results show that the coverage of titania has a great influence on microwave response of barium ferrite. The formation of an anatase titania nano-layer on the surface of a barium ferrite particle changes the character of the frequency dispersion of the complex permittivity. Comparing the anatase titania-coated barium ferrite composites with the uncoated barium ferrite, the complex permittivity of the anatase titania-coated barium ferrite composites is higher than that of uncoated barium ferrite. The complex permeability of composites was found to decrease with an increase in frequency as well as with the molar ratio of Ti:Ba. The enhancement of the complex permittivity may be due to dipolar polarization and interfacial polarization. The maximum reflection loss was obtained at the Ti:Ba ratio of 1:10, and the peak of the maximum reflection loss shifts to a lower frequency value with increasing titania fraction. By changing the thickness of titania coverage, the frequency dependence of the complex permittivity could be adjusted, which provides us an opportunity for the synthesis of tailored particles.