Superconductivity and calorimetric studies of Pr1.85Ce0.15CuO4+δ under different annealing conditions Original Research Article

Polycrystalline samples of electron-doped Pr1.85Ce0.15CuO4+δ have been prepared under different annealing conditions and investigated by means of X-ray-diffraction, oxygen content analysis, electrical resistivity, magnetic susceptibility and low temperature specific heat measurements. X-ray-diffraction patterns show that samples contain a single T′ phase. The superconducting transition temperatures Tcm taken with the onset of diamagnetism in magnetic-susceptibility measurements are 20 and 19.5 K for sample annealed in flowing Ar gas and in vacuum (∼10−3 torr), respectively. The data of the samples, which are annealed in flowing Ar gas, show clear evidence for an αT2 term at zero magnetic field in superconducting electronic specific heat, and are consistent with d-wave superconductivity. However, this behavior is not observed in the other sample, which is annealed in vacuum. These results indicate that different heat treatments affect the oxygen content, homogeneity, superconducting transition temperature Tc, superconducting volume fraction, and the superconducting pairing symmetry of Pr1.85Ce0.15CuO4+δ.