Effects of annealing temperature on structure and magnetic properties of amorphous Fe61Co27P12 nanowire arrays Original Research Article

Arrays of Fe61Co27P12 nanowire with an aspect ratio about 70 were prepared in anodic aluminum oxide templates by electrodeposition. The influences of annealing temperature on structure and magnetic properties of Fe61Co27P12 nanowires were studied. When the specimens were annealed below 400 °C, there are no obvious changes in structure except relaxation. With the annealing temperature increasing from 400 to 600 °C, the Fe–Co phase is detected by X-ray diffraction and Mössbauer spectra. The crystalline fraction and hyperfine field can be derived from Mössbauer spectra. The room temperature magnetic hysteresis loops show that the coercivity and squareness of the nanowire arrays in parallel to the wire axis increase with the increasing of annealing temperature, which mainly attributes to the strengthening of anisotropy.