Nitrogen containing barium titanate: Preparation and characterisation Original Research Article

The purpose of this work is to study the incorporation of nitrogen into barium titanate at oxygen sites by ammonolysis. The nitrogen content of the resulting barium titanate powders strongly depends on the flow rate of ammonia and the ratio Ba/Ti. The amount of resulting oxygen vacancies is lowered by co-doping with fluoride and tantalum. By avoiding an excess of BaO and exchanging 10 mol% Ti by Ta it is possible to produce powders with nitrogen content of more than 1 wt%. Partial substitution of barium oxide by barium fluoride also increases the nitrogen content. The nitrogen containing powders are colored and show an additional absorption at 500 nm measured in the UV/vis reflectance spectrum. The concentrations of nitrogen and fluorine in the samples were determined using ion-sensitive electrodes. X-ray powder diffraction shows the composition of the powders. The thermal stability was investigated by thermogravimetric analysis, and in order to calculate the specific surface area the three-point BET method was used.