Influence of grain size on the electrical properties of the double-layered LaSr2Mn2O7 manganite Original Research Article

The double-layered LaSr2Mn2O7 manganite was synthesized by the sol–gel process. Two samples with the average grain size from ∼150 nm to ∼1 μm were prepared by controlling the sintering temperature. Both samples had a tetragonal structure, with a small fraction of impurity phase in the S-1250 sample. In order to investigate the probable influence of grain size on the conduction mechanism, resistivity of the samples was measured as a function of temperature, and the data obtained was analyzed by different conduction mechanisms. It was found that with increase in the grain size, resistivity decreased at all temperature ranges. The results show that the adiabatic small polaron hopping (SPH) model is probably responsible for conduction at high temperature range, and that the 3D variable range hopping (VRH) model shows a better correlation with the experimental data for low temperature range. These analyses indicate the influence of grain size on the parameters obtained from fitting the data by both models.