Influence of pH condition on colloidal suspension of exfoliated graphene oxide by electrostatic repulsion

A facile chemical process is described to produce graphene oxide utilizing a zwitterions amino acid intermediate from graphite oxide sheets. 11-aminoundecanoic acid molecules were protonated to intercalate molecules into the graphite oxide sheets to achieve ion exchange, and the carboxyl groups were then ionized in a NaOH solution to exfoliate the graphite oxide sheets. In this way, the produced graphene oxide nanosheets were stably dispersed in water. The delaminated graphene nanosheets were confirmed by XRD, AFM, and TEM. XRD patterns indicated the d002-spacing of the graphite greatly increased from 0.380 nm and 0.870 nm. AFM and TEM images showed that the ordered graphite crystal structure of graphene nanosheets was effectively exfoliated by this method. The prepared graphene nanosheets films showed 87.1% transmittance and a sheet resistance of 2.1×103 Ω/square.