Influence of nanoinclusions on scattering of holes and phonons and transport coefficients in BixSb1−xTe3 bulk nanostructures

One of the possible ways to increase the thermoelectric figure of merit is the use of bulk nanostructured materials fabricated by melt spinning with subsequent hot pressing or spark plasma sintering. Among a variety of nanostructure types these materials contain regions of initial solid solution with nanometer sized inclusions of different compositions. In the present work the scattering of holes and phonons on nanoinclusions in such p-BixSb1−xTe3 based materials is considered. The change of transport coefficients due to this scattering mechanism is theoretically estimated. The estimations showed that the reduction of lattice thermal conductivity (about 12–13%) for nanoinclusions of Bi2Te3–Sb2Te3 solid solution with different compositions is much greater than the change in power factor. Therefore the corresponding increase of the thermoelectric figure of merit for this case is determined mainly by phonon scattering. Also it is shown that the results of estimations depend on phonon spectrum approximation, e.g. in the case of sine-shaped instead of linear phonon spectrum the estimations give two times higher thermal conductivity reduction.