Tritium release from neutron-irradiated Li2O sintered pellets: porosity dependence

The tritium release behaviour from sintered Li2O pellets of various densities (71–98.5% theoretical density, T.D.) has been investigated by heating tests at a constant rate. It is shown that the tritium release rate depends on porosity at densities above 87% T.D., while no dependence was observed at densities below 86% T.D. The tritium release process is thought to consist of three stages described as follows: (1) the liberation of tritium trapped at point defects due to their recovery (peak at around 570 K); (2) the advection through interconnected pores via adsorption and desorption on their inner walls and diffusion in the gas phase of interconnected pores (peak at around 620 K); (3) the dissolution and release of tritium trapped in closed pores (peaks at around 700, 830 and 1000 K).