Nafion–polyfurfuryl alcohol nanocomposite membranes for direct methanol fuel cells

Commercial Nafion 115 membranes were successfully modified by in situ acid-catalyzed polymerization of furfuryl alcohol (PFA) within Nafion structures. FT-IR and AFM were used to characterize the chemical and morphological structures of the Nafion–PFA nanocomposite membrane obtained. The methanol permeation experiments showed that the methanol flux through the Nafion–PFA nanocomposite membranes dropped by a factor of 2.2–2.7 when PFA loading was 3.9–8.0 wt.%. Importantly, the proton conductivity of the membranes decreased only slightly at a low PFA loading (<8 wt.%). The nanocomposite membranes with higher selectivity (e.g., proton conductivity/methanol crossover) achieved a much higher DMFC performance at both room temperature and 60 °C.