Fluence dependence of deuterium retention in oxidized SS-316

The ion fluence dependence of deuterium retention in SS-316 during oxidation at a temperature of 673 K was studied to evaluate the dynamics of deuterium retention in the oxide layer of SS-316. The correlation between the chemical state of stainless steel and deuterium retention was evaluated using XPS and TDS. found that the major deuterium desorption temperatures were located at around 660 K and 935 K, which correspond to the desorption of deuterium trapped as hydroxide. The deuterium retention increased with increasing deuterium ion fluence, since the deuterium retention as hydroxide increased significantly. However, retention saturated at an ion fluence of ∼2.5 × 1021 D+ m−2. The XPS result showed that FeOOD was formed on the surface, although pure Fe also remained in the oxide layer. These facts indicate the nature of the oxide layer have a key role in deuterium trapping behavior.