Effect of temperature on hardness of binary U–15%Pu alloy and T91 cladding

The high temperature hardness behaviour of U–15%Pu and T91 cladding was studied with the help of a hot hardness tester. The hardness versus temperature plot for the T91 alloy consists of two straight lines with different slopes intersecting at 778 K. The hot hardness data of orthorhombic α phase of U–15%Pu showed a transition at around 408 K. The appearance of the tetragonal β-phase showed a sudden increase in the hardness above 828 K. γ-Phase of U–15%Pu was found to very soft. Since U–15%Pu fuel is softer than the T91 cladding above 473 K, the probability of the clad damage by the fuel due to its interaction with the cladding is very less.