Hydride behavior in Zircaloy cladding tube during high-temperature transients

In order to study the hydride behavior in high burnup fuel cladding during temperature transients expected in anticipated operational occurrences and accidents, unirradiated hydrided Zircaloy-4 cladding tubes were rapidly heated to temperatures ranging from 673 to 1173 K and annealed for holding time ranging from 0 to 3600 s. Hydrides were localized in the peripheral region of the cladding tubes prior to the annealing, as observed in high burnup fuel cladding. The localized hydride layer (hydride rim) was annealed out, and the radial hydride distribution became uniform after the annealing at 873 K for 600 s, 973 K for 60 s, or 1173 K for 0 s. The annealing out of the hydride rim is caused by the phase transformation from the α + δ phase to the α + β or β phase in the hydride rim and the subsequent drastic increase in the solid solubility and diffusion of hydrogen in Zircaloy. On the other hand, the radial distribution and morphology of hydrides did not change at lower temperatures: Thus, the hydride remains almost intact below the phase transformation temperature for the short time ranges.