Evaluation of effect of hydrogen on toughness of Zircaloy-2 by instrumented drop weight impact testing

Hydride-assisted degradation in fracture toughness of Zircaloy-2 was evaluated by carrying out instrumented drop-weight tests on curved Charpy specimens fabricated from virgin pressure tube. Samples were charged to 60 ppm and 225 ppm hydrogen. Ductile-to-brittle-transition behaviour was exhibited by as-received and hydrided samples. The onset of ductile-to-brittle-transition was at about 130 °C for hydrided samples, irrespective of their hydrogen content. Dynamic fracture toughness (KID) was estimated based on linear elastic fracture mechanics (LEFM) approach. For fractures occurring after general yielding, the fracture toughness was derived based on equivalent energy criterion. Results are supplemented with fractography. This simple procedure of impact testing appears to be promising for monitoring service-induced degradation in fracture toughness of pressure tubes.