Crystallization kinetic of glass particles prepared from a mixture of coal ash and soda-lime cullet glass

The crystallization capability of a parent glass made from a mixture of coal ash (40 wt%) and soda-lime glass was investigated using differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy. Different glass particle size distributions were considered in the range 20–500 μm. Two crystallization exotherms in DTA were attributed to the formation of both pyroxenes (diopside Ca(Mg,Al)(Si,Al)2O6 and augite Ca(Mg,Fe)Si2O6) and plagioclase (Na,Ca)(Si,Al)4O8. These phases were confirmed by XRD analyses. Analysis of non-isothermal DTA data yielded values of 545 kJ/mol and 1.8 for the activation energy of crystallization and the Avrami exponent, respectively. This value for the Avrami exponent was consistent with a decreasing nucleation rate and the observed dendritic morphology. The data on crystallization kinetics obtained in this study are relevant for the production of glass-ceramic materials by a sintering/crystallization method from powder compacts made of this parent glass.