Electrical properties of A2.6+xTi1.4−xCd(PO4)3.4−x (A = Li, K; x = 0.0–1.0) phosphate glasses

Electrical properties of A2.6+xTi1.4−xCd(PO4)3.4−x (A = Li, K; x = 0.0–1.0) phosphate glasses are investigated over a frequency range from 42 Hz to 1 MHz at different temperatures. Impedance spectroscopy is used to separate the bulk conductivity from electrode effect of electrical conductivity data. The bulk dc conductivity is Arrhenius activated, with activation energies and pre-exponential factors following the Meyer–Neldel rule. The real part of ac conductivity shows universal power law feature. The variation of dielectric constant with frequency is attributed to ion diffusion and polarization occurring in the phosphate glasses. The frequency dependent imaginary part of electric modulus M″(ω) plot shows non-Debye feature in conductivity relaxation. The Kohlrausch–Williams–Watts stretched exponential function was used to describe the modulus spectra and the stretching exponent β is found to be temperature independent. Scaling in M″(ω) shows that the electrical relaxation mechanisms are independent of temperature for given composition at different temperatures.