Structural peculiarities, and electrical and optical properties of 70TeO2·30PbCl2 glasses doped with Pr3+, prepared in Pt or Au crucibles

The influence of crucibles (Au or Pt) on the structure, electrical, dielectric and optical properties of 70TeO2·30PbCl2 glasses doped with Pr3+ added as a metal, chloride, or oxide, in concentrations of 500–1500 wt-ppm, is reported. The dc conductivity of ‘pure’ glasses prepared in Au crucibles is two orders of magnitude higher than that of those prepared in Pt crucibles. Upon doping, the dc conductivity of glasses prepared in Pt and Au crucibles increases or decreases, respectively. The static relative permittivity is equal to 33 ± 2. In the range of 640–700 nm, six photoluminescence (PL) peaks were observed, at 641.5, 647.1, 652.4, 660.8, 662.9, and 664.5 nm. In the range of 200–1200 cm−1, seven Raman scattering (RS) peaks were observed at 184, 217, 321, 468, 654, 735 cm−1, and a small peak at 650 cm−1. Both spectra were deconvoluted using symmetrical Gaussian functions. Relative intensities of PL and RS bands depend on the concentration and chemical form of Pr3+ and on the material of the crucible. However, positions of these bands are independent of these conditions.