UV–visible and infrared absorption spectra of transition metals-doped lead phosphate glasses and the effect of gamma irradiation

Undoped and transition metals (TM 3d)-doped lead phosphate glasses were prepared. Ultraviolet–visible absorption spectra were measured in the range 200–1100 nm before and after successive gamma irradiation. Experimental results indicate that the undoped lead phosphate glass reveals before irradiation strong and broad ultraviolet absorption which is related to the co-sharing of absorption due to both trace iron impurities and lead ions (Pb2+). In the TM-doped glasses, characteristic absorption bands are obtained in both the UV and/or visible regions due to each respective TM ion in addition to that observed by the base undoped UV absorption. Gamma irradiation produces with the undoped glass a prominent induced ultraviolet broad band centered at about 300 nm originating mostly from the contribution of trace iron impurities and the visible spectra reveal markedly high shielding behavior towards successive gamma irradiation, due to the presence of both high content of heavy Pb2+ ions and the sharing of phosphate as a partner. With TM-doped samples, the observed induced bands are virtually varying and related to the type of the sharing TM ions. Infrared absorption spectra reveal in the undoped and TM-doped glasses characteristic structural phosphate groups mainly consisting of metaphosphate and pyrophosphate units. Transition metals are assumed to cause depolymerization of the phosphate glass network with different ratios but the changes in IR spectral data are limited due to the low doping level. Gamma irradiation of the samples is assumed to cause changes in the bond angles or bond lengths of the structural phosphate units within network as evident in the variation of the intensities of the IR bands.