Abstract :
The effect of Ni and Mo alloying additions on crystallization of an Fe–Si–B based amorphous alloy was studied by applying various experimental techniques – DSC, XRD and TEM. It was shown that both alloying additions Ni and Mo change the crystallization temperature as well as the activation energy of primary crystallization. The phases formed during primary crystallization for the Fe80Si6B14 and Fe78.5Ni1Mo0.5Si6B14 alloys were the same, however the morphologies were significantly different. The addition of 1.0 at.% of Ni and 0.5 at.% Mo changed the crystallization mechanism and the type of formed phases. Such additions also resulted in formation of nanocrystals. The kinetic and thermodynamic characteristics of annealed specimens of amorphous metallic Fe80Si6B14 and Fe78.5Ni1Mo0.5Si6B14 alloys were established. These characteristics were determined based on measurements of instantaneous changes of electrical strength. It was shown that the method of electromotive force measurements was more sensitive to structural changes and the phase composition of amorphous metallic electrodes in comparison with the X-ray method.