Shear bond strength of a hot pressed Au–Pd–Pt alloy–porcelain dental composite

Objectives: The purpose of this study was to evaluate the effect of hot pressing on the shear bond strength of a Au–Pt–Pd alloy–porcelain composite. s: Several metal–porcelain composites specimens were produced by two different routes: conventional porcelain fused to metal (PFM) and hot pressing. In the latter case, porcelain was hot pressed onto a polished surface (PPPS) as well as a roughened one (PPRS). Bond strength of all metal–porcelain composites were assessed by the means of a shear test performed in a universal test machine (crosshead speed: 0.5 mm/min) until fracture. Interfaces of fractured specimens as well as undestroyed interface specimens were examined with optical microscope, stereomicroscope, Scanning Electron Microscope (SEM) and Energy Dispersive X-Ray Spectroscopy (EDS). The data were analyzed using one-way ANOVA followed by Tuckey’s test ( p < 0.05 ). s: Shear bond strength of conventional PFM specimens were in line with the upper range of literature data (83±14 MPa). Hot pressing proved to significantly increase bond strength between metal and porcelain ( p < 0.05 ). For both polished and roughened surface the shear bond strength values for hot pressed specimens were 120±16 MPa and 129±5 MPa, respectively, which represents an improvement of more than 50% relatively to a conventional PFM. Roughened surface did not have a significant effect on bond strength of hot pressed specimens ( p > 0.05 ). icance: This study shows that it is possible to significantly improve metal–porcelain bond strength by applying an overpressure during porcelain firing.