Tape casting of nanocrystalline ceria gadolinia powder

A ceramic ceria gadolinia solid solution membrane for solid oxide fuel cells was fabricated by tape casting using a nanopowder of 37 nm average particle size. A novel combination of solvent and dispersant was used to disperse the nanoparticles. The polymer was added in a dilute stage to guarantee a homogeneous distribution. After casting a remarkable densification of the cast tape suspension from a solid loading of 20 up to 42 vol.% was observed during drying. The green tape was sintered to >92% theoretical density and was dense towards perfusion. The resulting grain size in the sintered specimen still was <200 nm.