Crack-healing behavior and resultant strength properties of silicon carbide ceramic

Silicon carbide (SiC) has good high temperature strength and resistance to radioactivity. However, it has poor fracture toughness. To overcome this weakness, a crack-healing ability is very desirable. This study focuses on the crack-healing behavior of commercial SiC ceramic. The crack-healing behaviors of SiC ceramic were investigated systematically, as a function of crack-healing temperature, time, crack size and temperature dependence of the resultant bending strength. Three-point bending specimens were made and a semi-elliptical crack was introduced on the specimen by a Vickers indenter. Pre-cracked specimens were healed at various conditions. All fracture tests were performed on a three-point loading system with a 16 mm bending span. The main conclusions obtained were: (1) optimized crack-healing condition is; temperature: 1773 K, 1 h in air. (2) The maximum crack size that can be healed completely under the optimized condition was semi-elliptical surface crack of 450 μm in diameter. (3) Limiting temperature for bending strength of crack-healed zone for bending strength was about 873 K.