Stabilization of zirconia lamellae in rapidly solidified alumina–zirconia eutectic composites

In-situ fabrication of ceramic eutectic composites by rapid solidification of eutectic drops is a cheap and quick method compared to directional solidification or to multi-step fabrication methods of fiber reinforced/layered materials for high temperature use. Binary eutectic composites with a homogeneous periodic microstructure have been obtained by directional solidification of eutectic melts for many years, but typical solidification velocities used in directional solidification are limited to the range of cm/hour or, more recently, up to 15 mm/min. The present study aims to determine the effects of faster solidification rates on the structure of the alumina–zirconia binary composites obtained at higher growth rates by rapid solidification from eutectic melts in air or vacuum. A binary composite with zirconia stabilized in the high-temperature tetragonal form is presented. The stabilization of the tetragonal phase has not been observed before in bulk crystalline pellets of binary Al2O3–ZrO2 eutectic composites.