We have studied the influence of increasing the amount of β-spodumene (LiAlSi2O6), as a Li2O-containing flux, on the phase composition, the microstructure evolution and the physical properties of high-alumina porcelain. Quartz reacts with β-spodumene in the temperature range 1150–1250 °C, forming lithium aluminium silicates with a larger amount of SiO2. The presence of lithium minerals contributes to a lower CTE for the fired bodies. At 1300 °C an improved flexural strength is achieved with compositions containing 1.0 or 1.2 wt.% of Li2O, as a result of a more uniform microstructure. With increasing amounts of Li2O the overfiring effect is greatly enhanced. The most favourable characteristics from an industrial perspective with regard to flexural strength and deformation during firing were attained by using a high-alumina porcelain composition containing 1.0 wt.% Li2O.