Preparation of concentrated barium titanate suspensions incorporating nano-sized powders

In order to reduce agglomeration and overcome the low packing density issues of working with nano-sized powders, a colloidal processing route has been chosen in this study. Commercial BaTiO3 (BT) powders with a particle size in the range of 50 nm have been dispersed in the aqueous media. Rheological properties have been analyzed on suspensions with different solids loading, dispersant concentration, and pH conditions. Optimum dispersing conditions were obtained for suspensions prepared at basic pH (pH 10) with 0.646 wt% ammonium poly (acrylic acid) (NH4PAA) as a dispersant. Suspensions have been centrifugally cast to obtain the green body, and the sintering conditions have been investigated by examining the phase evolution, microstructures and electrical properties of the sintered samples through XRD, SEM and dielectric measurements, respectively. The results show that for a 45 vol% suspension sintered at 1325 °C, the density of bulk ceramic can reach 5.85 g/cm3, nearly 97.0% of the theoretical density.