Dependence of dielectric properties on structural characteristics of (Zn1/3A2/3)0.5 (Ti1−xBx)0.5O2 (A = Nb5+, Ta5+, B = Ge4+, Sn4+) ceramics at microwave frequencies

The effects of structural characteristics on the dielectric properties of (Zn1/3A2/3)0.5(Ti1−xBx)0.5O2 (A = Nb5+, Ta5+, B = Ge4+, Sn4+) (0.1 ≤ x ≤ 0.3) ceramics were investigated at microwave frequency. The sintered specimens showed solid solutions with a tetragonal rutile structure within the solid solution range of compositions. With an increase of BO2, the temperature coefficient of resonant frequency (TCF) and dielectric constant (K) decreased with a decrease of oxygen octahedral distortion and dielectric polarizabilites, respectively. However, the quality factor (Qf) of the sintered specimens was increased with BO2 due to the reduction of Ti4+ ions. The Qf value of the specimens with A = Ta was higher than that of the specimens with A = Nb.