Fracture resistance of a doped PZT ceramic for multilayer piezoelectric actuators: Effect of mechanical load and temperature

The fracture resistance behaviour of a doped lead zirconate titanate (PZT) ceramic after combined thermo-mechanical loading is investigated between room temperature (RT) and 400 °C, i.e. above the Curie temperature (TC). The thermal- and stress-induced depolarisation effects due to domain switching have been assessed by the indentation method on bulk PZTs. This has been extended to multilayered actuators. Experimental findings show a depolarisation effect with the temperature, which is significantly enhanced when combined with mechanical loading. This partial or even full depolarisation of the PZT material below TC leads to important anisotropy effects in the fracture resistance of the piezo-ceramic, which should be taking into account in the design of multilayer actuators where the direction of crack propagation (i.e. parallel or normal to electrodes) can affect the actuator functionality.