Effects of SiO2 addition on TiO2 crystal structure and photocatalytic activity

A series of TiO2–SiO2 mixtures – having the following stoichiometry Ti1−xSixO2, with x = 0, 0.1, 0.3 and 0.5 atoms per formula unit – were prepared by using precursor oxides and fired at three temperatures (900, 1000 and 1200 °C). The modifications in the structure and, consequently, on the photocatalytic activity, induced by the addition of SiO2 into the TiO2 powder, were thoroughly investigated by using various analytical techniques: X-ray powder diffraction, electron microscopy (FE-SEM and TEM), XPS, FT-IR, DRS and BET analysis. The results underlined as essentially no solid solution occurs between the two crystalline end-members. Nevertheless, silica addition caused a retarding effect on anatase-to-rutile phase transformation and on the crystallite growth. otocatalytic activity of the powders was assessed in gas phase and the results were explained by taking into account the anatase and rutile relative amounts in the samples, their crystallite size, the surface hydroxyl groups adsorbed on the photocatalysts and the surface area of the mixtures.