Experimental determination of the eutectic temperature in air of the CuO–TiO2 pseudobinary system

Eutectic temperature and composition in the CuO–TiO2 pseudobinary system have been experimentally determined in air by means differential thermal analysis (DTA), thermogravimetry (TG) and hot-stage microscopy (HSM). Samples of the new eutectic composition treated at different temperatures have been characterized by X-ray diffraction (XRD) and X-ray absorption near-edge structural spectroscopy (XANES) to identify phases and to determine the Cu valence state, respectively. The results show that the eutectic temperature in air is higher by 100 °C (∼1000 °C) for a Ti-richer composition ( X TiO 2 = 25   mol % ) than the one calculated in the literature. The reduction of Cu2+ to Cu+ takes places at about 1030 °C. The existence of Cu2TiO3 and Cu3TiO4 has been confirmed by XRD in the temperature range between 1045 and 1200 °C.