The friction and wear of electroless Ni–P matrix with PTFE and/or SiC particles composite

In this paper, the friction behaviour and wear mechanism of electroless Ni–P matrix with PTFE and/or SiC particles composite coating are investigated by virtue of ring-on-disk wear machine at a high load of 150 N. The worn surface, wear debris and the composition changes after wear were characterized using scanning electron microscopy (SEM) and energy-dispersive analysis of X-ray (EDAX). By comparison with Ni–P and Ni–P–SiC coatings, the results indicated that the combination of a PTFE-rich mechanical mixed layer (PRMML) formed on the worn surface and hard SiC were responsible for the good tribological properties of the hybrid Ni–P–PTFE–SiC composites at high load. After heat treatment at 400 °C for 1 h, the wear rate of Ni–P matrix composites decreased with corresponding increase in microhardness. During sliding, an obvious decrease in the temperature rise with PTFE addition was attributed to the good anti-friction of PTFE.