Influence of pH on particle size and sensing response of chemically synthesized chromium oxide nanoparticles to alcohols

Nanoparticles of chromium oxide have been synthesized by following a co-precipitation route at various pH values of the precursor solution. Structural and morphological analysis were carried out by using XRD and TEM techniques which revealed that the size of nanoparticles synthesized at pH 9 was smaller as compared to those synthesized at other pH values. The thick films of synthesized samples were deposited on alumina substrate and their sensing response to methanol, ethanol and isopropanol was investigated at different operating temperatures. It was observed that all the sensors gave optimum response at 250 °C. It has been observed that sample prepared at pH 9, being a collection of smallest particles as compared to other samples, exhibited high sensing response to alcohol vapour. Sensor response of all the samples tested was significantly higher towards isopropanol vapour than towards methanol or ethanol. present study the effect of particle size on intergranular activation energy has been studied as well. It was found that smaller particles possess high activation energy and exhibit higher sensing response as compared to that of larger particles. This type of study may help in the selection of particle suitable for gas sensing.