Microstructure and tensile properties of orthorhombic Ti–Al–Nb–Ta alloys

Microstructure and tensile properties of orthorhombic Ti–Al–Nb–Ta alloys have been studied. In order to optimize ductility and strength of the orthorhombic alloys with the nominal compositions of Ti–22Al–23Nb–3Ta and Ti–22Al–20Nb–7Ta, various thermomechanical processing steps were implemented as part of the processing route. With a special heat treatment before rolling to obtain a fine and homogeneous rolled microstructure, the rolled microstructure resulted in a good combination of high tensile yield strength and good ductility of the alloys through available solution and age treatments. The duplex microstructure with equiaxed α2/O particles and fine O phase laths in a B2 matrix, deforming in α2+B2+O phase field and treating in O+B2 phase field, possesses the highest tensile properties. The R.T. yield strength and ductility of the Ti–22Al–20Nb–7Ta alloy are 1200 MPa, and 9.8% respectively. The yield strength and ductility values of 970 MPa and 14% were also maintained at elevated temperature (650°C).